products categories
- Battery Production Equipment Line
- Battery Lab Pilot Equipment Line
- Lithium Battery Pack Assembly Line
- Solid State Battery Assembly Line
- Sodium Ion Battery Production Line
- Supercapacitor Assembly Line
- Lithium Ion Battery Recycling Plant
- Dry Electrode Preparation Solution
- Perovskite Based Solar Cell Lab Line
- Li ion Battery Materials
- Battery
- Battery Pack Machine & Compoments
- Lithium Battery Machine
- Lithium Battery Production Plant
- Vacuum Glove Box
- Furnaces
- Coaters
- Hydraulic Press
- Ball Mill
- Planetary Centrifugal Mixer
- Cutting Machine
- Laboratory Machine
- Metal Foam
contact us
- If you have questions, please contact us, all questions will be answered
- WhatsApp : +86 13174506016
- Email : David@tmaxcn.com
- Email : Davidtmaxcn@gmail.com
- Add : No. 39, Xinchang Road, Xinyang, Haicang Dist., Xiamen, Fujian, China (Mainland)
products
99.9% Purity Aluminium Foil Roll For Battery Grade
Model Number:
TMAX-AL-16Compliance:
CE CertifiedPayment:
L/C D/A D/P T/T Western UnionDelivery Time:
2 days
- WhatsApp : +86 13174506016
- Email : David@tmaxcn.com
- Email : Davidtmaxcn@gmail.com
- Wechat : 18659217588
Previous:
Conductive Carbon Coated Aluminum Foil For Lithium Ion BatteryNext:
Aluminum Foil Double Side Coated by LiFePO4
Product Details
99.9% Purity Aluminium Foil Roll For Battery Grade
SPECIFICATION
Aluminum foil specification |
||
Item |
Type 1(T-AL-16) |
Type 2(T-AL-12) |
Width |
customized |
customized |
Thickness |
16±1 um |
12±1um |
Areal density |
42~46g/ m2 |
30~34g/m2 |
With transverse
surface density uniformity |
≤0.003 g/ 40×40 mm |
≤0.003 g/ 40×40 mm |
The same volume
of vertical surface density uniformity |
≤0.03 g/ 400×40 mm |
≤0.03 g/ 400×40 mm |
High temperature
oxidation resistance (200°C*30min) |
No oxidation |
No oxidation |
Connect no |
<2 |
<2 |
Chemistry
content(Al) |
>99.45% |
>99.45% |
Extensibility |
<0.5% |
<0.5% |
Normal
temperature Tensile strength kgf /mm2 |
>180 |
>140 |
After 1200C baking 1h,
Tensile strength kgf/mm2 |
>160 |
>120 |