Single Particle Force Properties Test System

Single Particle Force Properties Test System   Test Object Lithium battery anode and cathode electrode materials   Test Particle Size Single particle size: 5~50μm   Application 1. Testing the crushing strength of battery material particles 2. Can be used to evaluate the pressure resistance of the material 3. Guide the rolling process 4. Materials with high mechanical strength will have better subsequent cycle stability.   Product Introduction 1.Background Testing the crushing strength of battery material particles can be used to evaluate the pressure resistance of the material and guide the rolling process. Materials with high mechanical strength will have better subsequent cycle stability. 2. Testing Object Lithium battery positive and negative electrode materials(Positive: polycrystalline ternary; lithium-rich material; Negative: silicon-based, hard carbon, etc.; solid electrolyte)   3. Test Particle Size Single particle size: 5~50 um   4. Equipment Composition Testing Program 1. Testing Method Disperse the powder into the liguid., Add it dropwise to the glass slide. Locate the single particle under an optical microscope. Control the pressure head to press down at a constant speed. Collect the force and displacement curves during the particle compression process and calculate the mechanical properties of the single particle. 2. Test Parameters 1) Magnification: up to 1200 times; 2) Pressure test range: 0-100 mN; 3) Pressure test accuracy: ±0.1 mN; 4) Minimum displacement unit: 10 nm; 5) Data collection frequency: 1000HZ. 6) Comply with national standard GB/T 43091-2023″Powder Compressive strength Test Method”   Application Cases 1. Anode Material-Sic     1) Two silicon-carbon materials with different electrode compaction. 2) Comparison of crushing force distribution: A>B. 3) Analysis of stress-displacement curves: Sample A exhibits initialmicro-crackingfollowed by complete collapse, while sample B expe-riences direct structural collapse and fragmentation. 4) Comparison of Disintegration States: after fracturing, all three groups disintegrate into fine granular states.   Particle Compression Resistance and Powder Compaction   Case 1: Two Different Pure Carbons     The compressive resistance of particle level C1 is stronger. Corresponding to the powder end, C1has a higher compression modulus than C2, with both maximum deformation and irreversible deformation smaller than C2. Case 2: Three Different Carbon-Silicon Materials     SC-3 has weaker compressive strength of its particles, resulting in significantly larger maximum deformation and irreversible deformation when the powder is compressed compared to theother two materials.   2. Ternary Cathode Material-NCM811     Specifications